Compatibility characteristics of acellular porcine heart valve matrix co-crosslinked with procyanidins and glutaraldehyde

MA Xu-bing 1, ZHAI Wan-yin 2, ZHANG Jia-min 3, ZHU Zi-yan 3, ZHANG Hong-feng 1, CHANG Jiang 2   

  1. 1. School of Life Sciences, East China Normal University, Shanghai 200062, China; 2. State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; 3. Shanghai (Red Cross) Blood Center, Shanghai Institute of Blood Transfusion, Shanghai 200051, China
  • Received:2012-02-01 Revised:2012-05-01 Online:2013-03-25 Published:2013-03-20

PDF

2998

摘要： 采用8 mg/mL原花青素交联脱细胞猪主动脉心脏瓣膜4 h后，再经1.25 mg/mL戊二醛交联44 h.生物相容性检测结果显示，共交联瓣膜组细胞粘附率较戊二醛单独交联提高59%（(78.75±8.7)%～(19.75±3.27)%）、无明显溶血现象（(0.75±0.36)%）、血小板粘附量较戊二醛单独交联显著减少（（193±15.5）个 vs (292.6±24.93)个）、免疫原性低（(49.33±6.3)% vs (95.27±5.26)%）. 研究结果表明，共交联瓣膜材料有良好的细胞相容性、较好的血液相容性和较低的免疫原性，是一种优良的生物瓣材料，有望应用于生物瓣制备.

关键词: 原花青素, 戊二醛, 交联, 心脏瓣膜, 相容性

Abstract: The clinical used bioprosthetic heart valves (BHVs) were prepared from biological tissues by glutaraldehyde (GA) crosslinking. But the clinical application of BHVs is limited mainly due to calcification, cytotoxicity and remaining immunogenicity. Procyanidins (PC) can crosslink acellular heart valve matrix (AHVM) through hydrogen bond formation and prevent AHVM from calcification. The aim of this study is to modify GA crosslinking method using PC co-crosslinking to produce a much ideal material with higher compatibility for BHV preparation. Porcine aortic AHVM was crosslinked by 8 mg/mL PC for 4 h and then by 1.25 mg/mL GA for 44 h. The co-crosslinked AHVM was tested for cytocompatibility, blood compatibility and immunogenicity. The results showed that the in vitro adhesion rate of valvular interstitial cells on co-crosslinked AHVM was increased by 59% （78.75%～19.75%）when compared with that of GA-crosslinking. There was no difference in hemolysis between co- and GA- or PC-crosslinked AHVM. The co-crosslinked AHVM exhibited significant anti-thrombosis effect ((193±15.5) platelets) when compared with that of GA-crosslinked ((292.6±24.93) platelets). Furthermore, co-crosslinked AHVM displayed lower immunogenicity than that of GA-crosslinked ((49.33±6.3)% vs (95.27±5.26)%, cell adhesive rate). These results suggest that co-crosslinked AHVM has high potential to be used for preparation of BHVs.

Key words: procyanidins, glutaraldehyde, crosslinking, heart valve matrix, compatibility